PLA-WF semifinished plastic sheets rods hollow square solid bars |
 |
 |
|
Products -
PLA
|
BIOAKU PLA-WF Composite based on polylactic acid and wood fibres.
 High mechanical strength, due to the excellent bond
of the wood fibres to the polymer and the polymers to
each other.
Good thermal insulation
| BIOAKU |
|
|
PLA-WF |
| Technical properties |
Norm |
Unit |
|
| Physical properties |
|
|
|
| Maximum permissible service temperature |
- |
°C |
|
| Vicat softening temperature |
ISO 306 |
°C |
|
| Specific gravity |
ISO 1183 |
g/cm³ |
1,0 |
|
|
|
|
| Ecological properties |
|
|
|
| Ratio of renewable raw materials |
- |
% |
. 80 |
| Industrially compostable* |
- |
- |
Yes |
|
|
|
|
| Mechanical properties |
|
|
|
| Tensile strength at yield |
ISO 527 |
MPa |
42 |
| Elongation at yield |
ISO 527 |
% |
|
| Tensile stregth at break |
ISO 527 |
MPa |
41,5 |
| Elongation at break |
ISO 527 |
% |
|
| Shore-D |
ISO 179 |
kJ/m² |
|
| Modulus of elasticity |
ISO 527 |
MPa |
3510 |
| Impact stregth Charpy (23 °C) |
ISO 179 |
kJ/m² |
14,9 |
| Notched impact stregth Charpy (23 °C) |
ISO 179 |
kJ/m² |
3,7 |
|
|
|
|
| Thermal properties |
|
|
|
| Heat deflection temperature HDT/A |
ISO 75 |
°C |
72 |
|